Influence of peracetic acid at acrylic resin properties / Influência do ácido peracético nas propriedades de uma resina acrílica

PURPOSE: To evaluate the influence of peracetic acid immersion on water sorption, solubility and microhardness of heat and self-cured acrylic resins. METHODS: Thirty specimens of each type of acrylic resin were produced for sorption, solubility and microhardness evaluation. Sorption and solubility were evaluated based on ISO1567. For the microhardness test, specimens (20.0×5.0×10.0 mm) were made and evaluated under a 100 g load for 15 s. The test groups were submitted to a peracetic acid 0.2% immersion for 10 minutes. Data of sorption and solubility were analyzed by two way ANOVA and, hardness values, by paired t-test. RESULTS: Values of sorption and solubility were in agreement with ISO1567 requirements to both groups and ranged, in µg/mm³, for sorption from 22.28 (±4.40) to 24.25 (±3.27), and from 1.09 (±0.16) to 1.29 (±0.10) for solubility. Solubility showed a statistically significant difference between the two types of resin at test group. There was no statistical significant difference at the microhardness values. CONCLUSION: In this study, immersion in peracetic acid solution 0.2% showed no alterations at acrylic resin properties tested.Peracetic acid could be recommended to replace the conventional agents for the disinfection of acrylic resin devices.

OBJETIVO: Avaliar a influência da imersão em ácido peracético sobre a sorção, solubilidade e microdureza de resinas acrílicas termo e autopolimerizada. METODOLOGIA: Trinta corpos de prova de cada resina acrílica foram confeccionados para avaliação da sorção, solubilidade e microdureza. A sorção e a solubilidade foram avaliadas de acordo com a ISO 1567. Para a determinação da microdureza, os corpos de prova (20×5×10 mm) foram confeccionados e avaliados com uma carga de 100 g por 15 s. Os grupos teste foram imersos em ácido peracético 0,2% por 10 minutos. Os dados de sorção e solubilidade foram analisados com ANOVA de duas vias e de dureza por teste t pareado. RESULTADOS: Os valores de sorção e solubilidade ficaram de acordo com as especificações da ISO 1567 para ambos os grupos e no ensaio de sorção variaram entre 22,28 (±4,40) até 24,25 (±3,27), e de 1,09 (±0,16) até 1,29 (±0,10) para solubilidade, em µg/mm³. A solubilidade apresentou diferença estatisticamente significativa entre os dois tipos de resina após imersão em ácido peracético. Os valores de microdureza não apresentaram diferença estatisticamente significativa entre os grupos. CONCLUSÃO: A imersão em ácido peracético 0,2% não alterou as propriedades avaliadas das resinas acrílicas.

Avaliação da densidade óptica de três resinas compostas fotopolimerizáveis associadas à estrutura dental / Evaluation of tree composites optical density associated to dental structure

O objetivo deste estudo foi avaliar a densidade óptica de três resinas compostas fotopolimerizáveis com diferentes espessuras associadas à estrutura dental, através de programas para análise de radiografias digitalizadas. Utilizou-se um pré-molar humano superior extraído, seccionado no sentido mésio-distal. Foram confeccionados corpos de prova nas espessuras de 1, 2, 3 e 4 mm de cada material restaurador. De cada corpo de prova foram obtidas três radiografias periapicais padronizadas. As imagens foram digitalizadas e, por meio dos programas ImageLab v. 2.3, ImageTool v. 3.0 e Adobe Photoshop v. 6.0, foram obtidos os valores médios e os desvios padrão dos níveis de cinza em uma área padronizada do corpo de prova e da dentina do mesmo dente. A Análise de Variância Múltipla demonstrou não haver diferenças significativas na densidade óptica média tanto das resinas quanto da dentina em relação aos diferentes programas. O Teste de Comparações Múltiplas de Tukey demonstrou que, para todas as espessuras e resinas, a densidade média foi significativamente maior do que a da dentina e que nas resinas testadas a densidade óptica média, apesar de aumentar conforme a espessura do corpo de prova, não difere significativamente em relação à mesma. Diferenças estatisticamente significativas foram observadas entre os três materiais restauradores testados, independente da espessura do corpo de prova. A ordem crescente de densidade óptica encontrada foi: Durafill, Charisma e Z-250.

The aim of this study was to evaluate the optical density of three composites with different thicknesses, associated to the dental structure, through softwares for analysis digitized radiographies. For this, an human upper premolar, sectioned in the mésio-distal. Samples of 1, 2, 3, and 4 mm of thicknesses had been confectioned of each filling material. Of each sample three standardized periapical radiographies had been gotten. The images had been digitized and the average gray levels were obtained through the softwares ImageLab v. 2,3, ImageTool v. 3,0 and Adobe Photoshop v. 6,0., in a standardized area of the sample and the dentin of the same tooth. The Analysis of Multiple Variance, using the delineation block-type, found no significant differences in the average optical density neither for composites nor for dentin in relation to the different softwares. Complementing the analysis with the Test of Multiple Comparisons of Tukey, it is verified that, for all the thicknesses and composites, the mean density - or either the radiopacity - of the composite are significantly higher than the dentine. In all tested materials, the average optical density, although to increase as the thickness of the sample, does not differ significantly. Statistical significant differences had been observed between the three filling materials tested, independent of the thickness of the sample. The increasing order of optical density was: Durafill, Charisma, and Z-250.

Comparação de três sistemas digitais em relação à densidade óptica de cimentos de ionômero de vidro / Comparison of three digital systems in relation to the optical density of glass ionomer cements

Objetivo: O objetivo deste estudo foi comparar três sistemas digitais, dois do tipo placas ópticas e um sensor, quanto à densidade óptica de três cimentos de ionômero de vidro restauradores. Materiais e Método: Foram obtidas imagens radiogrßficas dos corpos de prova confeccionados com cada um dos materiais, em espessuras de 1, 2, 3 e 4 mm, posicionados entre as metades de um pré-molar humano, extraído e seccionado no sentido mésio-distal. As medidas de densidade óptica, em valores de pixels, foram realizadas de acordo com as especificações do sistema correspondente ao receptor de imagem utilizado e analisadas por meio do teste não-paramétrico de Friedman (α = 1%). Resultados: Os resultados mostraram diferenças significativas nas médias dos valores de densidade óptica entre os sistemas digitais. As maiores médias foram determinadas no sistema CYGNUS, seguido pelo DENOPTIX e menores valores para o DIGORA (p ≤ 0,01). Entretanto, não se observou diferenças estatísticas quando comparadas as médias das variações de densidade óptica decorrentes do aumento na espessura do corpo de prova. Conclusão: Portanto, pode-se concluir que, apesar de diferirem quanto aos valores de densidade óptica, os sistemas testados apresentam padrões semelhantes quando expressam a variação em função da espessura do material utilizado.

Avaliação da densidade óptica de três cimentos de ionômero de vidro associados à estrutura dental / Evaluation of three glass ionomer cements' optical density associated do dental structure

O objetivo deste trabalho foi avaliar a densidade óptica de três cimentos de ionômero de vidro restauradores (Vitro Fill, VidrionR e Vitremer), com quatro diferentes espessuras, associados à estrura dental, através de três programas para análise de radiografias digitalizadas. Para isto, utilizou-se um pré-molar humano superior, extraído por indicação ortodôntica, seccionado no sentido mésio-distal e incluído em 2 cm de resina acrílica autopolimerizável. Foram confeccionados corpos de prova de espessuras de 1 mm, 2 mm, 3 mm e 4 mm de cada material restaurador. De cada corpo de prova foram obtidas três radiografias periapicais padronizadas. As imagens foram digitalizadas e, através dos programas ImageLab v. 2.3, ImageTool v. 3.0 e Adobe Photoschop v. 6.0, foram obtidos os valores médios e os desvios padrão dos níveis de cinza em uma área padronizada do corpo de prova e da dentina do mesmo dente. Através da Análise de Variância Múltipla, utilizando o delineamento em blocos casualizados, ao nível de significância de 5 por cento, verifica-se não haver diferenças significativas na densidade óptica média tanto dos ionômeros quanto da dentina em relação aos diferentes programas. Complementando a análise com o Teste de Comparações Multiplas de Tukey, verifica-se que, para todas as espessuras e ionômeros, a densidade média, ou seja, a radiopacidade, do material é significativamente maior do que a da dentina e que nos ionômeros testados a densidade óptica média aumenta conforme a espessura do corpo de prova. Contudo, diferenças significativas foram encontradas somente para o Vitremer, comparando as espessuras 1, 2, e 3 mm à 4 mm. Nas espessuras de 1 a 3 mm não foram observadas diferenças estatisticamente significativas entre Vidrion e Vitremer, os quais foram significativamente menos radiopacos que o Vitro Fill. Na espessura de 4 mm, Vitremer apresentou-se significativamente mais radiopaco que o Vidrion e não diferiu significativamente de nenhuma das espessuras de Vitro Fill